Unique Brazed Clad Wear Plates of Super-Thick Tungsten Carbide with Nickel

Unique Sintered Super Wear Plate and Thermal Spraying Powders

Wires and Powders for Welding, Additive Manufacturing and 3D Printing

Unique Brazed Clad Wear Plates of Super-Thick
Tungsten Carbide with Nickel

1.Description

Unique super-thick brazed Cast Tungsten Carbide Clad Wear Plate with Nickel contains the steel base and the brazed clad layer of Nickel matrix with Cast Tungsten Carbide hard particles, which bonding strength is high enough. The wear resistance of the clad layer is very good owing to the Cast Tungsten Carbide hard particles are uniformly distributed in the Nickel matrix. And the steel base makes the clad plate very good strength as well.

1.1Chemical Composition

Cr	B	C	Si	Mo+Cu+Co	W+V	La+Ce+Yt	Ni
0-5%	0.5-5%	0.5-8%	0.04-5.5%	0-15%	0-60%	0-5%	Balance

Types

Cost

Wear Resistant

Wear Resistant Layer Thickness

Crack

Weight Loss

（mg）

Cost-effective

CWP-1

AAA

30mm

No Crack

AAA

60FTC

AAA

10mm

Cracks

1.2Application

The microstructure shows that Cast Tungsten Carbide hard particles uniformly dispersed in the matrix of martensite and residual austenite. The clad layer is very high abrasion resist and without cracks.

The abrasion resistance of our Nickel brazed Cast Tungsten Carbide clad wear plates can be close to the plasma deposit clad60% Cast or Fused Tungsten Carbide with 40% Nickel alloy powder, 60FTC (60%FTC+40%Ni40) by PTA plasma cladding, while the thickness of Nickel Cast Tungsten Carbide clad wear plates can be much thicker than 60FTC, greatly reduce downtime replace cost.

Our Nickel brazed Cast Tungsten Carbide clad wear plates can be widely used for replacing the Cement Carbide in the abrasion resistance of Oil Sand, Coal Mining Conical Bits, Cement Liner, Brick Mold etc.

2. Technical Data

Typical Length*Width:300 x 150 mm; Base Thickness: 2square+5chamfer=7mm；Clad Thickness:30 mm;
Base Metal: Mild Steel